Unidirectional prepreg

Products from remaining stock: Carbon fibre prepregs with epoxy resin 913 C

With epoxy resin 913 C: hardening at 125°C, at least 60 min, Storage time: 30 days at room temperature, 360 days at -18°C

Fibres Tenax HTA/HTS or Toray 300J
Yarn 12K-rovings arranged in parallel
Standard width of rolls 1270 mm
Thickness of layers 0.125 mm 0.250 mm
Areal weight of the prepreg 203 g/m² at 35% resin 406 g/m² at 35% resin
220 g/m² at 40% resin 440 g/m² at 40% resin
Areal weight of the fibres 132 g/m² 264 g/m²
  Longitudinal along fibre Perpendicular to fibre
Tensile strength 1950 MPa 75 MPa
Tensile modulus of elasticity 130 MPa 9100 MPa
Compressive strength 1500 MPa 230 MPa

with epoxy resins 6376, 977, M21, 8552

With epoxy resins 6376, 977, M21, 8552: hardening at 180°C, at least 120 min, Storage time: 21 days at room temperature, 180 days at -18°C

Fibres Tenax HTA/HTS or Toray 300J
Yarn 12K-rovings arranged in parallel
Standard width of rolls 1270 mm
Thickness of layers 0,125 mm 0,250 mm
Areal weight of the prepreg 203 g/m² at 35% resin 406 g/m² at 35% resin
220 g/m² at 40% resin 440 g/m² at 40% resin
Areal weight of the fibres 132 g/m² 264 g/m²
  Longitudinal along fibre Perpendicular to fibre
Tensile strength 1950 MPa 75 MPa
Tensile modulus of elasticity 130 MPa 9100 MPa
Compressive strength 1500 MPa 230 MPa